Color effect materials and production thereof

ABSTRACT

A color effect material is described as composed of a plurality of encapsulated substrate platelets in which each platelet is encapsulated with a highly reflective layer which acts as a reflector to light directed thereon and a spacer pigment layer which is selectively transparent to light directed thereon.

BACKGROUND OF THE INVENTION

The provision of metallic effects in surface coatings, plastics coloration, cosmetic preparations and the like is well known. To achieve this effect, one approach has been to disperse both a metallic pigment and a transparent colored pigment in the composition. The metallic pigment is usually aluminum flake and the colored pigment can be, for instance, iron oxide. The art has also combined the two pigments into a single entity by precipitating the colored material on the aluminum flake.

The precipitation of, for instance, iron oxide on the aluminum flake was often carried out from an aqueous solution but that gave rise to various difficulties. Aluminum readily reacts in aqueous media, very dilute solutions of the iron oxide were required, complexing additives were necessary and the procedure had to be carried out in a limited pH range.

An alternate, non-aqueous procedure is described in U.S. Pat. No. 4,328,042. Here, iron pentacarbonyl is oxidized to iron oxide and carbon dioxide in a fluidized bed of the aluminum flake with oxygen at elevated temperature. To obtain reproducible results, the carbonyl cannot exceed 5 volume percent of the fluidizing gas. The use of the low concentration carbonyl and fluidized bed operation are obvious drawbacks of this approach.

It is desirable to provide a color effect material (CEM) which has the same or better pigment properties as the products just mentioned but without encountering the production and materials limitations of that prior art. The present invention is directed to satisfying that desire.

SUMMARY OF THE INVENTION

The present invention provides a color effect material (CEM) comprising a platelet-shaped substrate encapsulated with: (a) a highly light reflective first layer of, e.g., silver, gold, platinum, palladium, rhodium, ruthenium, osmium, iridium, or an alloy thereof; (b) a spacer layer of metal oxide, nitride, fluoride or carbide or polymer; whose refractive index is sufficiently high to minimize the incident angle dependent variable pathlength difference, in accordance with Snell's Law, or thin enough to not be optically active; and optionally, (c) a light transparent layer which is either the same or a different metal as in the first layer or a spacer layer material different from that in the spacer layer and whose refractive index is higher than that of the spacer layer material. The CEM, where necessary, can be given a post-treatment for specific attributes such as weather stability, polymeric dispersability and cosmetic compatibility. The method of producing the CEM is also a part of this invention.

DESCRIPTION OF THE INVENTION

It is an object of the present invention to provide novel metal CEMs which can also be prepared in a reliable, reproducible and technically efficient manner. This object is achieved by a CEM comprising a platelet-shaped substrate coated with: (a) a highly light reflective first layer; (b) a spacer layer; and optionally, (c) a light transparent overlayer.

Any encapsulatable smooth platelet can be used as the substrate in this invention. Examples of usable platelets include mica, aluminum oxide, bismuth oxychloride, boron nitride, glass flake, iron oxide-coated mica, silicon dioxide and titanium dioxide-coated mica. The size of the platelet-shaped substrate is not critical per se and can be adapted to the particular use. In general, the particles have average largest major dimensions of about 5-250 microns, in particular 5-100 microns. Their specific free surface area (BET) is in general from 0.2 to 25 m²/g.

The degree of reflectivity for the first encapsulating layer, the highly reflective layer, should be at least about 75% and is preferably at least about 90% reflectivity. This layer may be constituted by one or more highly reflective metals such as silver, gold, platinum, palladium, rhodium, ruthenium, osmium and/or iridium or the alloys thereof. In the case of alloys, it is obvious that a near infinite number of alloys can be utilized in the present invention. A few alloy examples with their elemental constituents in parentheses are: sterling silver (silver and copper), coinage (gold and copper), rhodite (gold and rhodium), white gold (gold and palladium), yellow gold (gold, silver, copper, zinc and nickel) and gold plate (gold, silver and copper).

The thickness of the first layer is not critical so long as it is sufficient to make the layer highly reflective. If desirable, the thickness of the first layer can be varied to allow for some selective transmission of light. Depending on the metal or alloy utilized for the first encapsulating layer, the thickness can be about 2 to 100 nm and preferably about 10 nm to 75 nm. The mass percent of this coating can vary considerably because it is directly related to the surface area of the particular substrate being utilized and the thickness necessary to achieve the desired reflectivity. For example, if silver is selected as the component of the first layer, the thickness can be at least about 5 nm, preferably from about 10 to 75 nm. When gold is used, the thickness can be at least about 4 nm, preferably from about 10 to 70 nm. The thickness of platinum as the first layer can be at least about 3 nm, preferably from about 5 to 65 nm. A thickness of a layer of these metals outside of the above-mentioned ranges will typically be either completely opaque or allow for substantial transmission of light.

In addition to their reflective properties, the metals may exhibit unique bulk color effects depending on the film thickness. For example, thin semi-transparent films of gold may appear more violet in color similar to the purple of Cassius. Gold leaf of less than 100 nm, which is less than the 350-700 nm wavelength of white light, appears bluish green when viewed by transmitted light.

The first encapsulating layer may also be constituted by a plurality of different layers of the above-mentioned materials to obtain the desirable effect. For example, one may deposit a thin semi-transparent layer of gold on top of a reflective silver layer.

The CEM of the present invention contains a spacer layer encapsulation of the first encapsulating layer. The spacer layer is usually composed of metal, metal oxide, nitride, fluoride, or carbide or polymer. One can utilize any material for the spacer layer as long as it does not result in more than 100 degrees of hue angle color travel in accordance with Snell's Law. Examples of suitable materials include chromium oxide, silicon dioxide, magnesium fluoride, magnesium oxide, magnesium hydroxide, aluminum oxide, aluminum hydroxide, zinc oxide, zinc hydroxide, zirconium oxide, zirconium hydroxide, zirconium nitride, titanium oxide, titanium hydroxide, titanium nitride, iron oxide, iron hydroxide and polymers such as polymethyl methacrylate, polyethylene terephthalate and high density polyethylene. Preferably, the material is silicon dioxide (SiO₂), a suboxide of silicon dioxide (SiO_(0.25) to SiO_(1.95)) or magnesium fluoride.

The spacer layer material and the thickness of the layer are selected such that the layer does not provide a significant incident angle dependent variable pathlength difference in accordance with Snell's Law, i.e., does not result in more than 100 degrees of hue angle color travel. Therefore, the particular thickness of the layer is not important so long this criteria is met. One convenient way to met this requirement is to make the layer suitably thin. For example, materials having a refractive index around 1.5 should have a film thickness of no more than 60 nanometers so as to not generate hue angle color travel of more than 100 degrees. When the layer is of silicon dioxide or magnesium fluoride, it preferably has a thickness of about 25 to 50 nm. For a layer material having a high refractive index, such as for iron oxide, the layer can be any thickness sufficient to produce the desired result.

Incident angle dependent variable pathlength difference is related to the degrees of hue angle change when changing the view from normal incidence to a high specular angle. The thickness of the layer, its refractive index, and Snell's law all contribute to the incident angle dependent variable pathlength difference. The pathlength, which determines the color, is calculated by the equation 2(n)(d)Cos θ₂, where n is the refractive index, d is the thickness in nm and θ₂ is the refraction angle. The refraction angle θ₂ is determined by Snell's law n₁Sin θ₁=n₂Sin θ₂, where n₁ is the refractive index of the incident medium (here the reflecting layer), n₂ is the refractive index of the (spacer) layer, and θ₁ is the incident angle. A spacer layer with high refractive index would therefore not produce large differences in θ₂ with increasing θ₁ and would not produce significant pathlength differences. A layer with a low refractive index on the other hand, would produce large differences in θ₂ with increasing θ₁ and would produce significant pathlength differences unless the layer thickness is too thin to produce thin film interference. Thus, the spacer layer will not produce a significant incident angle dependent variable pathlength difference when it has a high refractive index and/or it is too thin to produce thin film interference. The purpose of the spacer layer is to provide non-limiting decorative and/or functional attributes such as color, adhesion promotion, and film stress relief.

The optional, outer encapsulating layer, when present, is a material providing a transparency of about 25-75% transmission. More preferably, one would prefer to have about 40-60% transparency for the outer encapsulating layer. The degree of reflectivity and transparency for the different layers can be determined using a variety of methods such as ASTM method E1347-97, E1348-90 (1996) or F1252-89 (1996), all of which are substantially equivalent for the purposes of this invention.

The material employed as the outer layer can be selected from the same group as the materials of the reflecting layer. Alternatively, the outer layer may also be a metal oxide, nitride or carbide provided that it is different than that of the spacer layer and also has a higher refractive index.

The CEMs of the invention are notable for multiple encapsulation of the platelet-shaped substrate. In one embodiment, the first layer and the spacer layer are additionally encapsulated by a selectively-transparent outer layer that allows for partial reflection of light directed thereon. Preferably, the outer encapsulating layer is selected from the group consisting of silicon, iron oxide, chromium oxide) a mixed metal oxide, titanium dioxide, titanium nitride, zirconium nitride and aluminum, so as the refracive index is higher than the spacer layer. More preferably, the outer layer is one or more of the precious metals or alloys of the first (reflecting) layer.

The optional outer layer is, of course, a part of the optical package. Its thickness can vary but must always allow for partial transparency. For instance, the layer has a preferable thickness of about 5 to 20 nm for silicon; about 2 to 15 nm for aluminum; about 1-15 nm for titanium nitride; about 10 to 100 nm for iron oxide; about 10 to 60 nm for chromium oxide; about 10-100 nm for titanium dioxide; about 5 to 60 nm for a mixed metal oxide, about 5 to 20 nm for silver; about 3 to 20 nm for gold; about 3-20 nm for platinum; and about 5 to 20 nm for palladium. The metal alloys generally have a similar film thickness compared to the pure metal. It is recognized that a film thickness out of the above range may be applicable depending on the desired effect.

All the encapsulating layers of the CEM of the invention are altogether notable for a uniform, homogeneous, film-like structure that results from the manner of preparation according to the invention.

An advantage realized by the present invention is that one does not have to start with a traditional metal flake which may have structural integrity problems, hydrogen outgassing problems and a host of other perceived issues (pyrophoric and environmental concerns) typically associated with metal flakes. The substrate contributes structural integrity and the metals used in this invention are much more chemically stable than aluminum and generally prefer to be in their non-oxidized metallic ground state. Furthermore, silver is preferred when employed as one of the reflecting layers, as it can maximize the chromaticity of the reflected color(s) of the CEM. In addition, when silver is used as the final (outer) layer of the particle, it may impart electrical conductivity to the CEM which may be desirable in some applications such as powder coatings.

While the metal layers can be deposited by any known means, they are preferably deposited by electroless deposition and the non-metal layers preferably by aqueous or non-aqueous sol-gel deposition An advantage of electroless deposition (Egypt. J. Anal. Chem., Vol. 3, 118-123 (1994)) is that it is a worldwide established chemical technique, not requiring cumbersome and expensive infrastructure compared to other techniques. The electroless deposition technique also allows one to control the degree of reflectivity of light quite accurately and easily by varying the metal film thickness. Additionally, the known procedures are generalized procedures capable of being utilized for coating a variety of surfaces. Furthermore, a layer of a metal or metal nitride can also be deposited onto any of the substrates by chemical vapor deposition from an appropriate precursor (The Chemistry of Metal CVD, edited by Toivo T. Kodas and Mark J. Hampden-Smith; VCH Verlagsgesellschaft mbH, D-69451 Weinheim, 1994, ISBN 3-527-29071-0).

The products of the present invention are useful in automotive, cosmetic, industrial or any other application where metal flake, pearlescent pigments or absorption pigments are traditionally used.

In the novel process for preparing the coated platelet-like substrates, the individual coating steps are each effected by known procedures such as by electroless deposition or hydrolysis/condensation of suitable starting compounds in the presence of the substrate particles to be coated. For instance, metals can be deposited from reduction of aqueous salts of the metals, such as HAuCl₄, AgNO₃, H₂PtCl₆ and PdCl₂. Silicon dioxide can be deposited from silicon tetraalkoxides such as tetraethoxysilane, bases such as sodium silicate and halide silanes such as silicon tetrachloride; titanium dioxide from tetraalkoxides such as titanium isopropoxide and titanium tetraethoxide, halide compounds such as titanium tetrachloride and sulfate compounds such as titanium sulfate, titanium nitride from titanium tetrachloride, tetrakis(diethylamido) titanium (TDEAT) and tetrakis(dimethylamido)-titanium (TDMAT); iron oxide from iron carbonyl, iron sulfate, iron nitrate and iron chloride; and chromium oxide from chromium carbonyl and chromium chloride.

In general, the synthesis of the color effect material can be as follows: a platelet material such as mica is suspended while stirring in an aqueous medium. The platelet substrate acts as a carrier substrate. It may, or may not, have a contribution or effect on the final optical properties of the particulate. To the suspension is added a metal precursor capable of depositing the desired metal (or alloy) on the substrate by electroless deposition, along with a suitable reducing agent. The resulting highly reflective metal coated substrate is filtered, washed and re-suspended in an alcoholic medium such as butanol. A Stöber process can be employed for the deposition of a silicon dioxide spacer layer on the metal coated mica or other substrate (C. Jeffrey Brinker and George W. Scherer, Sol-Gel Science, The Physics and Chemistry of Sol-Gel Processing, Academic Press, Inc. (1990)). An alcoholic azeotropic mixture, such as ethanol and water, may be used in place of pure alcohol for the Stöber process. The silica encapsulated metal coated platelet is filtered, washed and resuspended in a stirred aqueous medium. An aqueous solution of a metal salt is added and the pH is changed to deposit the metal salt on the spacer layer. Then to the aqueous medium, a metal solution for electroless deposition is added as described above allowing for the deposition of a selectively transparent metal coating. The final particulate product is washed and dried.

The color effect materials (CEMs) of the invention are advantageous for many purposes, such as the coloring of paints, printing inks, plastics, glasses, ceramic products and decorative cosmetic preparations. Their special functional properties make them suitable for many other purposes. The CEMs with a conductive outerlayer, for example, could be used in electrically conductive or electromagnetically screening plastics, paints or coatings or in conductive polymers. The conductive functionality of these CEMs makes them have great utility for powder coating applications.

Products of this invention have an unlimited use in all types of automotive and industrial paint applications, especially in the organic color coating and inks field where deep color intensity is required. For example, these CEMs can be used in mass tone or as styling agents to spray paint all types of automotive and non-automotive vehicles. Similarly, they can be used on all clay/formica/wood/glass/metal/enamel/ceramic and non-porous or porous surfaces. The CEMs can be used in powder coating compositions. They can be incorporated into plastic articles geared for the toy industry or the home. These CEMs can be impregnated into fibers to impart new and esthetic coloring to clothes and carpeting. They can be used to improve the look of shoes, rubber and vinyl/marble flooring, vinyl siding, and all other vinyl products. In addition, these colors can be used in all types of modeling hobbies.

The above-mentioned compositions in which the compositions of this invention are useful are well known to those of ordinary skill in the art. Examples include printing inks, nail enamels, lacquers, thermoplastic and thermosetting materials, natural resins and synthetic resins. Some non-limiting examples include polystyrene and its mixed polymers, polyolefins, in particular, polyethylene and polypropylene, polyacrylic compounds, polyvinyl compounds, for example polyvinyl chloride and polyvinyl acetate, polyesters and rubber, and also filaments made of viscose and cellulose ethers, cellulose esters, polyamides, polyurethanes, polyesters, for example polyglycol terephthalates, and polyacrylonitrile.

For a well-rounded introduction to a variety of pigment applications, see Temple C. Patton, editor, The Pigment Handbook, volume II, Applications and Markets, John Wiley and Sons, N.Y. (1973). In addition, see for example, with regard to ink: R. H. Leach, editor, The Printing Ink Manual, Fourth Edition, Van Nostrand Reinhold (International) Co. Ltd., London (1988), particularly pages 282-591; with regard to paints: C. H. Hare, Protective Coatings, Technology Publishing Co., Pittsburgh (1994), particularly pages 63-288. The foregoing references are hereby incorporated by reference herein for their teachings of ink, paint and plastic compositions, formulations and vehicles in which the compositions of this invention may be used including amounts of colorants. For example, the CEM may be used at a level of 10 to 15% in an offset lithographic ink, with the remainder being a vehicle containing gelled and ungelled hydrocarbon resins, alkyd resins, wax compounds and aliphatic solvent. The CEM may also be used, for example, at a level of 1 to 10% in an automotive paint formulation along with other pigments which may include titanium dioxide, acrylic lattices, coalescing agents, water or solvents. The CEM may also be used, for example, at a level of 20 to 30% in a plastic color concentrate in polyethylene.

In the cosmetic field, the CEMs can be used in all cosmetic and personal care applications subject, of course, to all regulatory requirements. Thus, they can be used in hair sprays, face powder, leg-makeup, insect repellent lotion, mascara cake/cream, nail enamel, nail enamel remover, perfume lotion, and shampoos of all types (gel or liquid). In addition, they can be used in shaving cream (concentrate for aerosol, brushless, lathering), skin glosser stick, skin makeup, hair groom, eye shadow (liquid, pomade, powder, stick, pressed or cream), eye liner, cologne stick, cologne, cologne emollient, bubble bath, body lotion (moisturizing, cleansing, analgesic, astringent), after shave lotion, after bath milk and sunscreen lotion.

For a review of cosmetic applications, see Cosmetics: Science and Technology, 2nd Ed., Eds: M. S. Balsam and Edward Sagarin, Wiley-Interscience (1972) and deNavarre, The Chemistry and Science of Cosmetics, 2nd Ed., Vols 1 and 2 (1962), Van Nostrand Co. Inc., Vols 3 and 4 (1975), Continental Press, both of which are hereby incorporated by reference.

Some illustrative examples of the invention will now be set forth. In these, as well as throughout this specification and claims, all parts and percentages are by weight and all temperatures are in degrees Centigrade, unless otherwise indicated.

EXAMPLE 1

One hundred grams of 100 micron glass flakes (100 micron average major dimension) is placed in a 1 liter beaker equipped with a magnetic stir bar and containing 393 grams of a 2% dextrose solution. The slurry is stirred at room temperature.

To the slurry is rapidly added a solution which is prepared as follows: 7.87 grams of silver nitrate crystals are dissolved into 375 ml distilled water using a magnetic stirrer. A 29% solution of ammonium hydroxide is added dropwise to the beaker resulting in a brown precipitate which redissolves at a higher concentration of the ammonium hydroxide solution. At the point where the solution becomes clear again, 5 extra drops of the ammonium hydroxide solution is added to ensure excess.

Several changes in the shade of the slurry occur as the reaction proceeds. After 15 minutes of stirring, the supernatant liquid is tested for silver ion by the addition of a few drops of concentrated hydrochloric acid. The test is a visual assessment of any precipitate and/or turbidity of which none is found. The slurry is filtered and rinsed several times with distilled water and the presscake is dried at 100° C. to a constant mass. The dried sample is a lustrous, opaque and silver colored material.

EXAMPLE 2

The silver coated borosilicate flakes prepared in Example 1 (0.9 kg; average particle size 100 microns) are loaded into a horizontal cylindrical mechanical mixer equipped with mixing blades on a cantilever shaft. A sparger is introduced through the side of the reactor for introduction of reactants. The reactor is heated to 200° C. and nitrogen is added at 168 standard cubic feet per hour (SACH) through the door end of the reactor. Nitrogen is bubbled through a sealed reservoir of iron pentacarbonyl (IPC) at 5 SCFH resulting in an addition rate of 0.32 g/min of IPC. This reagent flow is combined with an additional 238 SCFH of nitrogen as it enters the sparger which gives a total sparger gas flow of 243 SCFH. The run is continued for 5 hrs and color progression advances with the iron oxide layer thickness. A sample is periodically removed from the reactor demonstrating the color progression as a function of time, exhibiting colors ranging from bronze, copper and russet to golden green.

EXAMPLE 3

125 grams of silver coated glass flake (produced as set forth in Example 1) is slurried in 300 ml distilled water in a 1L round-bottom flask at 300 rpm and heated to 50° C. Then 300 ml of 0.19 M Fe(NO₃)₃ ^(·)9 H₂O is added at 0.3 ml/min. while maintaining a pH of 4.0 with 5% NH₄OH. At the end of the addition (approx. 16 hours), the sample is heated to 90° C. for 4 hours. The sample is then filtered hot, washed and dried at room temperature. The sample exhibits a unique golden bronze color.

EXAMPLE 4

A thin silica spacer layer is applied to a reflective metal coated substrate as follows. In a 3 l flask, 600 g of the silver coated borosilicate flake prepared in Example 1 is slurried in 1028 ml of 2-propanol. To the slurry is added 8 ml of 29% ammonium hydroxide and 64 ml of distilled water. The mechanically stirred slurry is heated to 60° C., at which time 33.2 g of tetraethoxysilane is added. After about 20 hours, the slurry is cooled, filtered, and washed with a few 100 ml aliquots of 2-propanol. The coated product is dried for 24 hours at 120° C.

EXAMPLE 5

In a 3 l flask, 200 g of the product prepared in Example 4 is slurried in 500 ml of distilled water and heated to 75° C. The pH is lowered to 5 using 15% acetic acid. A solution of 22.5% Fe(NO₃)₃ ^(·)9H₂O is added at 0.25 ml/min. Once the pH reached 3.5, 10% NaOH is used to hold the pH constant. Approximately 400 ml of the iron(III) nitrate solution is added. The resulting sample is filtered, washed, and dried at 200° C. yielding a highly reflective gold colored effect material.

EXAMPLE 6

Example 5 is repeated except that approximately 600 ml of the iron(III) nitrate solution is added. The resulting sample is filtered, washed, and dried at 200° C. yielding a highly reflective golden orange colored effect material.

EXAMPLE 7

Example 5 is repeated except approximately 800 ml of the iron(III) nitrate solution is added. The resulting sample is filtered, washed, and dried at 200° C. yielding a highly reflective golden orange colored effect material.

EXAMPLE 8

A thin titania spacer layer is applied to a reflective metal coated substrate as follows. In a 3 l flask, 100 g of silver coated borosilicate flake prepared in Example 1 is slurried in 1200 ml of ethanol. To the slurry is added 1.14 g of 39% hydrochloric acid and 70 ml of distilled water. Then 69 g of titanium tetraisopropoxide is added to the mechanically stirred slurry. After about 24 hours, the slurry is filtered, and washed with a few 100 ml aliquots of ethanol. The coated product is dried for 24 hours at 200° C.

EXAMPLE 9

A thin titania spacer layer is applied to a reflective metal coated substrate as follows. In a 5 l flask, 100 g of silver coated, borosilicate flake prepared in Example 1 is slurried in 3600 ml of ethanol. To the slurry is added 3.42 g of 39% hydrochloric acid and 210 ml of distilled water. Then 207 g of titanium tetraisopropoxide is added to the mechanically stirred slurry. After about 24 hours, the slurry is filtered, and washed with a few 100 ml aliquots of ethanol. The coated product is dried for 24 hours at 200° C.

EXAMPLE 10

The electroless silver method of Example 1 is used to produce a 5 nm thick silver third layer on 100 g of the product of Example 8.

EXAMPLE 11

A CEM prepared according to example 1 is incorporated into polypropylene step chips at 1% concentration. The step chips are appropriately named since they have graduating thickness at each step across the face of the chip. The graduating steps allow one to examine the different effect of the CEM based on polymer thickness.

EXAMPLE 12

A CEM prepared according to example 1 is incorporated into a nail enamel. 10 g of the CEM is mixed with 82 g of suspending lacquer SLF-2, 4 g lacquer 127P and 4 g ethyl acetate. The suspending lacquer SLF-2 is a generic nail enamel consisting of butyl acetate, toluene, nitrocellulose, tosylamide/formaldehyde resin, isopropyl alcohol, dibutyl phthalate, ethyl acetate, camphor, n-butyl alcohol and silica and 127P is a moderately viscous, nitrocellulose lacquer containing butyl acetate, toluene, nitrocellulose, tosylamide/formaldehyde resin, isopropyl alcohol, dibutyl phthalate, ethyl acetate, camphor, n-butyl alcohol and methoxypropanol acetate.

EXAMPLE 13

In a similar fashion, a CEM prepared according to example 1 is incorporated into a non-nitrocellulose based nail enamel. 10 g of the CEM is mixed with 82 g of Avalure AC 315 polymer, an acrylic polymer in ethanol, and acetone used in place of nitrocellulose.

EXAMPLE 14

A 10% by weight CEM from example 1 is sprayed in a polyester TGIC powder coating from Tiger Drylac using a PGI corona Gun #110347. The CEM is mixed in a clear polyester system and sprayed over a RAL 9005 black powder sprayed base. The CEM is highly attracted to the ground metal panel. Additionally, due to its high affinity to orient closely to the surface, it produces a finish that is high in distinctness of image (DOI). It does not require an additional clear coat to reduce protrusion often caused by traditional pearlescent (effect) and metal flake pigments.

EXAMPLE 15

A 10% dispersion of the CEM prepared according to example 1 is mixed into a clear acrylic urethane basecoat clearcoat paint system DBX-689 (PPG) along with various PPG tints to achieve desired color. The tint pastes consist of organic or inorganic colorants dispersed at various concentrations in a solventborne system suitable with the DMD Deltron Automotive Refinish paint line from PPG. The complete formulation is sprayed using a conventional siphon feed spraygun onto 4×12 inch (about 10×30 cm) curved automotive type panels supplied by Graphic Metals. The panel is clear coated with PPG 2001 high solids polyurethane clear coat and air dried.

Various changes and modifications can be made in the process and products of the invention without departing from the spirit and scope thereof. The various embodiments disclosed herein were for the purpose of illustration only and were not intended to limit the invention. 

What is claimed is:
 1. A color effect material comprising a platelet-shaped substrate sequentially encapsulated with: a first layer which is highly reflective to light directed thereon and which is selected from the group consisting of silver, gold, platinum, palladium, rhodium, ruthenium, osmium, iridium and alloys thereof; and a second spacer layer which does not provide significant incident angle dependent variable pathlength difference, said spacer layer being selected from the group consisting of silicon dioxide, magnesium fluoride, magnesium oxide, magnesium hydroxide, aluminum oxide, aluminum hydroxide, titanium oxide, titanium hydroxide, and iron oxide.
 2. The color effect material of claim 1, wherein the substrate is selected from the group consisting of mica, aluminum oxide, bismuth oxychloride, boron nitride, glass flake, iron oxide-coated mica, silicon dioxide and titanium dioxide-coated mica.
 3. The color effect material of claim 1, wherein the first encapsulating layer is silver.
 4. The color effect material of claim 1, wherein the first encapsulating layer is gold.
 5. The color effect material of claim 1, wherein the first encapsulating layer is platinum.
 6. The color effect material of claim 1, wherein the first encapsulating layer is palladium.
 7. The color effect material of claim 1, wherein the first encapsulating layer is said alloy.
 8. The color effect material of claim 1, wherein the spacer layer is encapsulated by an outer layer that is selectively transparent to light directed thereon.
 9. The color effect material of claim 8, wherein said selectively transparent layer is selected from the group consisting of silicon dioxide, titanium dioxide, iron oxide, chromium oxide, aluminum, aluminum oxide and a mixed metal oxide.
 10. The color effect material of claim 1, wherein the first layer is an electroless deposition layer.
 11. The color effect material of claim 1, wherein the spacer layer is silicon dioxide.
 12. The color effect material of claim 9, wherein the spacer layer is a sol-gel deposition layer.
 13. The color effect material of claim 1, wherein the substrate is platelet-shaped mica, the highly reflective first encapsulating layer is silver and the spacer layer is a selectively transparent layer of iron oxide.
 14. The color effect material of claim 8, wherein the substrate is platelet-shaped mica, the highly reflective first encapsulating layer is silver, the spacer layer is silicon dioxide and the outer encapsulating layer is a selectively transparent layer of iron oxide.
 15. A method of making a color effect material comprising: coating a platelet-shaped substrate with a first encapsulating layer highly reflective to light directed thereon and selected from the group consisting of silver, gold, platinum, palladium, rhodium, ruthenium, osmium, iridium and alloys thereof; and encapsulating the first layer with a spacer layer which does not provide significant incident angle dependent variable pathlength difference, said spacer layer being selected from the group consisting of silicon dioxide, magnesium fluoride, magnesium oxide, magnesium hydroxide, aluminum oxide, aluminum hydroxide, titanium oxide, titanium hydroxide, and iron oxide.
 16. The method of claim 15, wherein the substrate is selected from the group consisting of mica, aluminum oxide, bismuth oxychloride, glass flake, silicon dioxide, iron oxide-coated mica, titanium dioxide-coated glass and titanium dioxide-coated mica.
 17. The method of claim 16, further comprising encapsulating the spacer layer with an outer layer selected from the group consisting of silver, gold, platinum, palladium, alloys of said metals, silicon dioxide, iron oxide, chromium oxide, a mixed metal oxide and aluminum.
 18. The method of claim 15, wherein the spacer layer is silicon dioxide.
 19. A cosmetic preparation containing a colorant wherein the colorant is a color effect material of claim
 1. 20. A coating formulation containing a colorant wherein the colorant is a color effect material of claim
 1. 21. A plastic formulation containing a colorant wherein the colorant is a color effect material of claim
 1. 